原标题：多孔陶瓷材料生产工艺简介

方泰多孔陶瓷材料生产工艺简介:

1、材料混合：纳米氧化铝粉末，发泡剂，粘合剂和色粉的混合。

2、成型机的挤出：为了满足发泡剂的孔径和孔，将压力调节至合适的成型压力。

3、高温炉的烧结：为了满足发泡剂和细孔的孔径，根据适当的时间和温度控制烧结过程。

4、材料通风的测量：材料通风的质量将决定微孔陶瓷卡盘的质量。

5、水刀切割形状：去除了多余的材料，以提高精磨效率。

6、粗磨厚度：首先去除过多的材料以提高精磨效率。

7、精磨形状：确保形状的尺寸符合组合精度。

Fountyl Porous ceramics:

Material mixing: mixing of nano-alumina powder, foaming agent, binder and toner.

Extrusion of the molding machine: In order to meet the pore diameter of the foaming agent and pores, the pressure is adjusted to an appropriate pressure for molding.

High-temperature furnace sintering: In order to meet the pore size of the foaming agent and pores, the sintering process is controlled according to the appropriate time and temperature.

Measurement of material ventilation: The quality of material ventilation will determine the quality of micro porous ceramic chuck.

Waterjet cutting shape: Excessive material is removed to improve the efficiency of fine grinding.

Rough grinding thickness: Remove too much material first to improve the efficiency of fine grinding.

fine grinding shape: ensure that the size of the shape meets the combined accuracy.